Bai, M., Yang, L., Li, J. et al. (3 more authors) (2021) Mechanical and tribological properties of Si and W doped diamond like carbon (DLC) under dry reciprocating sliding conditions. Wear, 484-485. 204046. ISSN 0043-1648
Abstract
The mechanical and tribological properties of three types of diamond like carbon (DLC) coatings, i.e., non-doped, Si-doped, and W-doped DLC, are evaluated. Dry reciprocating sliding wear tests were performed to evaluate the effect of sliding frequency/velocity on friction, adhesion, and wear. The degree of graphitization of non-doped and W-doped DLC increases with sliding velocity, which results in a lower coefficient of friction (COF), and a decrease in wear rate. Si-doped DLC, however, exhibits distinct friction behaviour, with increasing COF and severe fluctuations in friction at higher sliding velocities. In Si-DLC frictional heating drives the formation of an oxide-rich tribofilm and large amounts of Si-rich oxide wear debris that are both adhesive and abrasive. The oxide-rich tribofilm, and lack of surface graphitization, result in the severe fluctuations of Si-DLC friction via stick-slip and surface fracture/wear mechanisms, and significantly increased COF and wear rates at higher sliding velocities.
Metadata
Item Type: | Article |
---|---|
Authors/Creators: |
|
Copyright, Publisher and Additional Information: | © 2021 The Authors. Published by Elsevier B.V. This is an open access article under the CC BY license (http://creativecommons.org/licenses/by/4.0/). |
Keywords: | Diamond like carbon; Doping; Thin film; Friction; Wear; Reciprocating |
Dates: |
|
Institution: | The University of Sheffield |
Academic Units: | The University of Sheffield > Faculty of Engineering (Sheffield) > Department of Materials Science and Engineering (Sheffield) |
Funding Information: | Funder Grant number Engineering and Physical Sciences Research Council EP/R001766/1 |
Depositing User: | Symplectic Sheffield |
Date Deposited: | 15 Oct 2021 06:31 |
Last Modified: | 15 Oct 2021 06:31 |
Status: | Published |
Publisher: | Elsevier BV |
Refereed: | Yes |
Identification Number: | 10.1016/j.wear.2021.204046 |
Open Archives Initiative ID (OAI ID): | oai:eprints.whiterose.ac.uk:179259 |