Double-glow plasma (DGP) coatings are recommended for metallic components to mitigate the damage induced by complex working conditions in previous studies. In this paper, Nb-rich (Cr–Nb₄) and Cr-rich (Cr₄–Nb) -alloyed layers were formed onto the Ti–Al substrate via a DGP process to enhance its wear resistance. Scratch and Nano-indentation tests were used to evaluate the mechanical properties of the coatings. The tribological behaviour of the coatings were investigated using a pin-on-disc tribometer by rubbing against the GCr15 ball. Results from surface analysis techniques showed that the coatings mainly comprised Cr, Nb and Cr₂–Nb phases, and were well bonded to the substrate. The hardness of the Cr–Nb₄ coating was 11.61GPa and the Cr₄–Nb coating was 9.66 GPa which all higher than that of the uncoated Ti–Al which was 5.65 GPa. However, the critical load of the Cr₄–Nb coating ~21.64 was higher than that of the Cr–Nb₄ coating ~17.6. And the specific wear rate of Cr–Nb₄ coating, Cr₄–Nb coating and uncoated Ti–Al were 3.54 × 10−⁴, 0.01 × 10−⁴ and 1.53 × 10−⁴mm³ N−¹ m−¹, respectively. The low-wear mechanism of the coatings is discussed in detail in this paper.
CORE (COnnecting REpositories)
CORE (COnnecting REpositories)