Thermal transitions in metastable Cu – 68.5 at. % Co alloy

Arc melted and drop tube processed Cu – 68.5 at. % Co alloy has been subjected to differential thermal analysis (DTA). The liquidus temperature determined from the DTA curves in the arc melt sample (1664 K) was found to be close to phase diagram estimate of 1662 K. In contrast as a result of liquid phase separation in the drop tube samples, the values obtained in the powders were much lower mainly because the compositions of the demixed phases vary from that of the parent melt. The liquidus temperature of the 850 + μm powders was 1632 K while that of the < 38 μm sieve size powder was 1616 K. This variance is due to the asymmetric nature of the metastable phase diagram of the system.