Kearney, S.A. orcid.org/0000-0002-1895-502X, McLuckie, B., Webb, K. et al. (7 more authors) (2020) Effects of plutonium dioxide encapsulation on the physico-chemical development of Portland cement blended grouts. Journal of Nuclear Materials, 530. 151960. ISSN 0022-3115
Abstract
The effects of alpha radiation on cementitious systems used for nuclear waste encapsulation, and the subsequent physico-chemical properties, have been subject to limited investigation comparative to the effects of gamma and neutron irradiations. This paper outlines an assessment of the impact of PuO2 incorporation on the bulk characteristics of BFS and PFA blended Portland cements, with specific focus on the microstructure, phase assemblage and the radiolysis of pore water. Cellulose was also added to the cements to investigate the effects of organics on these systems. Characterisation of the bulk phase assemblage and microstructure were completed using optical and scanning electron microscopy (SEM), x-ray diffraction (XRD), and thermogravimetric analysis (TGA). Gas evolution was measured to determine the radiolytic breakdown of pore solution. In all samples the PuO2 appeared well encapsulated, with good physical contact to the cement grout and no large scale defects observed. Pu-containing hydrates were not observed, but PuO2 containing BFS based systems showed variations in the ratio of sulfate-containing phases, with increased ettringite observed. Gas evolution results were consistent with expectations based on likely radiation deposition, and increased G(H2) values were observed for cellulose containing samples. The findings of this study suggest the investigated cements are suitable encapsulants matrices for wastes containing PuO2.
Metadata
Item Type: | Article |
---|---|
Authors/Creators: |
|
Copyright, Publisher and Additional Information: | © 2019 Elsevier B.V. This is an author-produced version of a paper subsequently published in Journal of Nuclear Materials. Uploaded in accordance with the publisher's self-archiving policy. |
Keywords: | Cement encapsulation; Plutonium; Radiolysis; Microstructural and phase assemblage changes |
Dates: |
|
Institution: | The University of Sheffield |
Academic Units: | The University of Sheffield > Faculty of Engineering (Sheffield) > Department of Materials Science and Engineering (Sheffield) |
Depositing User: | Symplectic Sheffield |
Date Deposited: | 28 Feb 2020 17:06 |
Last Modified: | 17 Dec 2020 01:38 |
Status: | Published |
Publisher: | Elsevier BV |
Refereed: | Yes |
Identification Number: | 10.1016/j.jnucmat.2019.151960 |
Open Archives Initiative ID (OAI ID): | oai:eprints.whiterose.ac.uk:157813 |
Download
Filename: PuO2_Manuscript_181119_Revised_V2 clean.pdf
Licence: CC-BY-NC-ND 4.0