Wind turbine gearbox operates under a wide array of highly fluctuating and dynamic load conditions caused by the stochastic nature of wind and operational wind turbine controls. Micropitting damage is one of failure modes commonly observed in wind turbine gearboxes. This article investigates gear micropitting of high-speed stage gears of a wind turbine gearbox operating under nominal and varying load and speed conditions. Based on the ISO standard of gear micropitting (ISO/TR 15144-1:2010) and considering the operating load and speed conditions, a theoretical study is carried out to assess the risk of gear micropitting by determining the contact stress, sliding parameter, local contact temperature and lubricant film thickness along the line of action of gear tooth contact. The non-uniform distributions of temperature and lubricant film thickness over the tooth flank are observed due to the conditions of torque and rotational speed variations and sliding contact along the gear tooth flanks. The lubricant film thickness varies along the tooth flank and is at the lowest when the tip of the driving gear engages with the root of the driven gear. The lubricant film thickness increases with the increase of rotational speed and decreases as torque and sliding increase. It can be concluded that micropitting is most likely to initiate at the addendum of driving gear and the dedendum of driven gear. The lowest film thickness occurs when the torque is high and the rotational speed is at the lowest which may cause direct tooth surface contact. At the low-torque condition, the varying rotational speed condition may cause a considerable variation of lubricant film thickness thus interrupting the lubrication which may result in micropitting.
CORE (COnnecting REpositories)
CORE (COnnecting REpositories)