In this study, changes in the adsorbed amount and surface structure of sodium hexametaphosphate (SHMP) were investigated for aluminum-doped TiO₂ pigment undergoing milling. Relaxation NMR was utilized as a potential at-line technique to monitor the effect of milling on surface area and surface chemistry, while XPS was used primarily to consider the dispersant structure. Results showed that considerable amounts of weakly adsorbed SHMP could be removed with washing, and the level of dispersant removal increased with time, highlighting destructive effects of sustained high-energy milling. Nonetheless, there were no significant chemical changes to the dispersant, although increases to the bridging oxygen (BO) peak full width at half-maximum (FWHM) suggested some chemical degradation was occurring with excess milling. Relaxation NMR revealed a number of important features. Results with unmilled material indicated that dispersant adsorption could be tracked with pseudo-isotherms using the relative enhancement rate (Rsp), where the Rsp decreased with dispersant coverage, owing to partial blocking of the quadrupolar surface aluminum. Milled samples were also tracked, with very accurate calibrations of surface area possible from either T₁ or T₂ relaxation data for systems without dispersant. Behavior was considerably more complicated with SHMP, as there appeared to be an interplay between the dispersant surface coverage and relaxation enhancement from the surface aluminum. Nevertheless, findings highlight that relaxation NMR could be used as a real-time technique to monitor the extent of milling processes, so long as appropriate industrial calibrations can be achieved.
CORE (COnnecting REpositories)
CORE (COnnecting REpositories)