Effects of temperature and curing duration on the stability of slag cements in combined chloride-sulphate environments

This experimental study investigates the effects of temperature and curing duration on the stability of slag blended cement systems exposed at 20 °C and 38 °C to combined sodium chloride (30 g/L)-sodium sulphate (3 g/L) solutions. Two slags, designated as slag 1 and 2, having CaO/SiO2 ratios of 1.05 and 0.94, were respectively blended with Portland cement CEM I 52.5R at 30 wt.% replacement level. Mortar prisms and cubes with w/b ratio of 0.5 and binder/aggregate ratio of 1:3 were then prepared for length and mass changes. The samples were cured in lime water for either 7 or 28 days before ponding for a total exposure period of 544 days. Analogous paste samples were also prepared to follow changes in the hydration products using X-ray diffraction (XRD). The results showed that curing at 38°C resulted in less expansion and prolonged curing generally reduced expansion except for slag 1 blend at 20 °C. Also, mass-change was minimal at 38 °C compared to 20 °C, and curing up to 28 days further improved mass stability. There was a positive correlation between mass change and length change for the period of investigation.