In some commercial titanium extrusion practices, twisting of the extrudate can occur, which can result in the need to crop the back and front end of the extruded material, thereby reducing yield and increasing material losses. Understanding more about the behaviour of material during the extrusion process, and investigating the cause of defects such as twisting by use of finite element (FE) modelling techniques could help to reduce these losses, improve the productivity of the extrusion process, and the overall quality of the material produced. One of the most important components of FE techniques for hot deformation is the type of flow stress model that is used in the simulations. In this investigation isothermal uniaxial compression testing was performed on cylindrical specimens of Ti-6Al-4V at temperatures ranging from 950 °C to 1200°C and strain rates of 0.1 s-1 to 50 s-1, to produce true stress against true strain and load against die travel curves which were subsequently used to develop a new specific flow stress model for use in hot deformation above the beta transus, which can ultimately be applied to the hot extrusion of Ti-6Al-4V. From analysis of this data it was concluded that flow softening and work hardening do not occur during deformation, and that low friction conditions exist between the material and the tooling. The activation energy for deformation was found to be 193178 J.mol-1, and the flow stress model was shown to give a good fit to the raw data at low strain rates, but this relationship broke down at higher strain rates. Finally the importance of generating a flow stress model specific to a particular operation, and set of experimental data, rather than relying on existing data available in the literature is demonstrated.
CORE (COnnecting REpositories)
CORE (COnnecting REpositories)