Wang, D. orcid.org/0000-0001-6957-2494, Zhou, D., Song, K. et al. (3 more authors) (2019) Cold‐sintered C0G multilayer ceramic capacitors. Advanced Electronic Materials, 5 (7). 1900025. ISSN 2199-160X
Abstract
Multilayer ceramic capacitors (MLCCs) based on (Bi0.95Li0.05)(V0.9Mo0.1)O4‐Na2Mo2O7 (BLVMO‐NMO), with εr = 39, temperature coefficient of capacitance, TCC ≈ ±0.01%, and tan δ = 0.01 at 1 MHz, are successfully fabricated by a cold‐sintering process at 150 °C. Scanning electron microscopy of the MLCCs combined with EDS mapping, X‐ray diffraction, and Raman spectroscopy reveals well‐laminated and undistorted dielectric layers composed of BLVMO and NMO discrete phases separated by Ag internal electrodes. Prototypes show comparable properties to C0G MLCCs (TCC = ±30 ppm °C−1 from −55 to +125 °C) currently commercially fabricated at 1100 °C using CaZrO3‐based dielectrics with glass sintering aids and Ni internal electrodes.
Metadata
Item Type: | Article |
---|---|
Authors/Creators: |
|
Copyright, Publisher and Additional Information: | © 2019 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim. This is an author-produced version of a paper subsequently published in Advanced Electronic Materials. Uploaded in accordance with the publisher's self-archiving policy. |
Keywords: | capacitors; cold sintering; microwave dielectric ceramics; MLCCs |
Dates: |
|
Institution: | The University of Sheffield |
Academic Units: | The University of Sheffield > Faculty of Engineering (Sheffield) > Department of Materials Science and Engineering (Sheffield) |
Depositing User: | Symplectic Sheffield |
Date Deposited: | 14 May 2019 13:46 |
Last Modified: | 03 Dec 2021 08:28 |
Status: | Published |
Publisher: | Wiley |
Refereed: | Yes |
Identification Number: | 10.1002/aelm.201900025 |
Open Archives Initiative ID (OAI ID): | oai:eprints.whiterose.ac.uk:146042 |