Surface modification of the laser sintering standard powder polyamide 12 by plasma treatments

Polyamide 12 (PA12) powder was exposed for up to 3 h to low pressure air plasma treatment (LP‐PT) and several minutes by two different atmospheric pressure plasma jets (APPJ) i.e., kINPen (K‐APPJ) and Hairline (H‐APPJ). The chemical and physical changes resulting from LP‐PT were observed by a combination of Scanning Electron Microscopy (SEM), Hot Stage Microscopy (HSM) and Fourier transform infrared spectroscopy (FTIR), which demonstrated significant changes between the plasma treated and untreated PA12 powders. PA12 exposed to LP‐PT showed an increase in wettability, was relatively porous, and possessed a higher density, which resulted from the surface functionalization and materials removal during the plasma exposure. However, it showed poor melt behavior under heating conditions typical for Laser Sintering. In contrast, brief PJ treatments demonstrated similar changes in porosity, but crucially, retained the favorable melt characteristics of PA12 powder.