Drying Simulated Advanced Gas Reactor Fuel: Proving the Concept

Spent Nuclear Fuel (SNF) reprocessing is due to cease in the UK in 2018 and a new interim storage method may be required if it is found that pond storage is not viable beyond the 25 year period which is currently understood to be safe. Dry storage has been used elsewhere in the world for Zircaloy and aluminium clad fuel and has been proposed for use in the UK, however since the UK’s fuel is predominantly stainless steel (SS) clad, testing will need to be carried out to ensure that drying methods are suitable. This will require representative samples for macro scale drying tests. To date little long term stored fuel has been examined. As a result, work has been carried out to try and ascertain whether the corrosion associated with long term storage leads to significant bound water and whether through wall cracks can be formed in intact lengths of SS tube.

It was found that unlike an aluminium simulant, corroded SS showed no sign of water loss as a result of oxide dehydration during controlled drying by thermogravimetric analysis, and consequently bound water could be disregarded. It was also found that through wall cracks could be produced in an intact length of SS tube which would be suitable for macro scale drying tests.

Some initial macro scale drying tests have been carried out using an alternative test piece with preformed cracks, and three distinct drying regimes to complete drying have been detected.