Composites of graphite nanoplatelets (GNPs) and rubbery epoxy (RE) resins as adhesives and pads are evaluated as thermal interface materials (TIM). GNP-15 and GNP-5 (15 and 5 µm across, respectively) were loaded in RE by 3-roll milling to produce GNP/RE composites. The role of composite processing techniques on the texture, thermal and electrical conductivities and compression properties of composites was studied and compared. Scanning electron microscopy revealed uniform dispersion of GNPs in RE, regardless of loading and X-ray diffraction texture measurement showed less platelet alignment in the composites at low loadings. Thermal conductivities of 20 wt% GNP-15/RE (3.29 W/m K) and 35 wt% GNP-5/RE composite (2.36 W/m K) were both significantly higher than pure RE (0.17 W/m K). GNP/RE retained good compliance, compressive moduli at 20 wt% loading being comparable to commercial BN/silicone TIM. Although thermal contact resistance of GNP/RE was higher than for commercial paste, its interfacial thermal transport outperformed GNP/silicone (due to RE’s strongly adhesive nature) and, across thick bond lines, outperformed reported GNP-pastes. The 20 wt% GNP-15/RE thermal pad had significantly lower thermal contact resistance than other GNP/RE pads. This decreased with increasing applied pressure, being comparable to commercial BN/silicone pad. GNP/RE composites are thus promising candidates for thermal interface adhesives and pads.
CORE (COnnecting REpositories)
CORE (COnnecting REpositories)