Effects of Using Alternative Extreme Pressure (EP) and Anti-Wear (AW) Additives with Oxy-Nitrided Samples

Oxy-nitriding is a widely used industrial process aiming to improve the tribological properties and performance of components. Previous studies have shown the effectiveness of the treatment with friction and wear performance, but very few have focussed on optimising this behaviour. The lubrication properties of several EP and AW additives were examined to investigate their effectiveness in improving the tribological properties of the layers formed after treatment. Previous studies showed the presence of an oxide layer on the sample could improve the effectiveness of the sulphurised olefin (SO) and tricresyl phosphate (TCP) additives. The friction and wear behaviour of oxy-nitrided samples were analysed using a tribometer and surface profiler. Scanning electron microscope, energy-dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy were employed to identify the morphologies and chemical compositions of the treated surface before and after testing. No real effect on friction was observed when using the SO or TCP additives, mostly due to lack of interaction with the less reactive iron nitride layer and their roles as anti-wear additives. However, when the zinc dialkyldithiophosphate-containing lubricant was used, a higher friction coefficient was observed. Greater improvements in anti-wear properties with the presence of additives in comparison with only using base oil were reported, with the TCP additive producing the lowest wear rates. The study effectively demonstrated that the additive package type used could impact the tribological and tribochemical properties of oxy-nitrided surfaces.